Abstract: This study was designed to investigate the weathering characteristics of Calabrian pine (Pinus brutia) wood. The wood specimens were impregnated with some copper-based chemicals and then varnish coated. As copper-based chemicals, Celcure C4, Korasit KS, and Tanalith E 8000 were used for impregnation. Polyurethane varnish (PV) and water-based varnish (WBV) were used as coating materials. Firstly, Calabrian pine wood was impregnated with 2,5 % and 5 % aqueous solutions of chemicals then coated with PV and WBV. Impregnated and coated Calabrian pine wood specimens were subjected to 6 months of natural weathering in Muğla, Turkey. After weathering, surface hardness, surface roughness, and adhesion strength changes of Calabrian pine wood specimens were determined. Impregnation caused to increase in surface hardness values of Calabrian pine. Surface hardness increases of WBV coated Calabrian pine specimens were higher than that of PV coated Calabrian pine specimens. Impregnation resulted in higher surface roughness values of Calabrian pine specimens. PV coated Calabrian pine specimens gave higher surface roughness than that of WBV coated Calabrian pine specimens. The adhesion strength values of all treatment groups were decreased after weathering. In general, adhesion strength decreases of WBV coated Calabrian pine specimens were higher than that of PV coated Calabrian pine specimens. The concentration levels of chemicals did not have a significant effect on surface roughness and adhesion strength of Calabrian pine wood after weathering.

Abstract The study investigates the gloss and color changes values of Calabrian pine (Pinus brutia Ten.) wood impregnated with some copper content impregnation chemicals such as Celcure C4, Korasit KS, and Tanalith E 8000 and then water-based varnish (WBV) and polyurethane varnish (PV) coated after 6 months of weathering. The results of study showed that gloss values of PV coated Calabrian pine wood were higher than that of WBV coated Calabrian pine wood before weathering. The gloss values of all treatment groups decreased after weathering. Lightness values of Calabrian pine wood also decreased for all treatment groups after weathering. Pre-impregnation before PV coating resulted in lower ��L* values of Calabrian pine wood. While all treatment groups tended to turn reddish by giving ��a* positive values, they tended to turn bluish by giving negative ��b* values. The lowest total color change was obtained with only WBV coated Calabrian pine wood.